Norland Optical Adhesive 63 ("NOA63") is a clear, colorless, liquid photopolymer that will cure when exposed to ultraviolet light. Since it is a one part system and 100% solids,it offers many advantages in bonding of optical elements where the bonding surface can be exposed to light. The use of NOA 63 eliminates premixing, drying or heat curing operations common to other optical adhesive systems. Curing time is remarkably fast, and is dependent upon the thickness applied and the amount of ultraviolet light energy available.

NOA 63 is recommended for the bonding of achromats, prisms and all other precision compound optics. The outstanding characteristics of the adhesive are its low fluorescence and its excellent transmission in the near UV range. After full cure, the adhesive has good transmission from 320 to 3,000 nanometers.

This adhesive is also suitable for bonding glass to metal. The high viscosity of NOA 63 allows it to be applied as a self-supporting drop or bead along the edge of a precision component to bond it to the substrate. The adhesive cures well in thick sections and has low shrinkage and a slight resiliency to minimize strain.

NOA 63 is cured by ultraviolet light with maximum absorption in the range of 350 to 380 nanometers. The recommended energy required for full cure is 4.5 Joules/sq. cm of long wavelength UV light.

 

Recommended Light Sources

HAND HELD MANUFACTURER CURE AREA APPROX. CURE TIME
Opticure LED 200
Norland Products
Cranbury, NJ
1/2 inch 5-10 seconds at 1/2 inch
DESK TOP MANUFACTURER CURE AREA

APPROX. CURE TIME

Bench Mount Lamp

Spectronics Westbury, NY
4 x 15 inches 40 minutes at 6 inches
                                                                                                                  Some of the light sources that can be used to cure the adhesive are sunlight, mercury lamps, and fluorescent blacklights.

 

 

In most optical applications, curing is done in two steps. First a short exposure, or precure, is used. This cures the adhesive enough to allow it to be handled without disturbing the alignment and keeps the number of alignment fixtures to a minimum. At this time, parts can be inspected and excess adhesive can be cleaned up with an acetone or alcohol moistened cloth. Any rejected pieces are most easily separated at this stage. Cure is completed by exposure for the remainder of the cure time.

The NOA bond can be separated in chlorinated solvent such as methylene chloride. The bonded area must be soaked in the solvent and normally will separate overnight if only precured. Longer times may be necessary depending upon the extent of the cure and the size of the bond area.

The NOA 63 can withstand temperatures of-15 to 60° C when used to bond glass optics. In some cases temperatures to 90° C are possible when the adhesive is used as a film or coating. The latter would depend upon the application.

 

Typical Properties of NOA 63

Solids100%
Viscosity at 25° C2000 cps
Refractive Index of Cured Polymer1.56
Elongation at Failure 6%
Modulus of Elasticity (psi)240,000
Tensile Strength (psi)5,000
Hardness - Shore D90


Shelf life of the liquid is a minimum of 6 months from the date of shipment, refer to the package label for the actual expiration date, if stored in a cool (5-22° C), dark place in the original container. If refrigerated, allow the ahesive to come to room temperature prior to use.

Care should be taken in handling this material. The Material Safety Data Sheet should be read for this product as well as for any associated products such as alcohol, acetone or methylene chloride. Prolonged contact with skin should be avoided and affected areas should be thoroughly washed with copious amounts of soap and water. If the adhesive gets into eyes, flush with water for 15 minutes and seek medical attention. Use the material in a well ventilated area, otherwise a NIOSH approved organic vapor mask is recommended.

Spectral Transmission of NOA 63

[Click Here To View MSDS Information]

 

Home - Adhesives - Fiber Optics - Fish Gel - Distributors - About - Trade Shows - Employment -